FJN-9 Organosilicone Resin |
| I Composition |
|
It is net structure POLYDIMETHYLSILOXANE toluene liquid treating silicon-oxygen bond and organic corps as side bond and can be cross linked and solidified under function of different assistant agents and certain temperature. Meanwhile, this resin is thermosetting type resin with high cross linking, high rigidity, high mechanical intensity, good resistance to high temperature and oxidation, good performance of electric insulation, excellent dampproofing ability, burning retardant and less smoke. It can be used as bonding agent of heat resistant isinglass plate, filling and sealing materials and heat resistant dope for resistor.
|
| II Main Technical Index |
Item |
Index |
Appearance |
Light yellow or yellow transparent even liquid, no mechanical impurity, slightly white light is permissible |
Solid Content % ≥ |
50 |
Viscidity（coat-4cups） S 25℃ |
8~35 |
Gelling Period 200℃ min |
2~20 |
|
| III Applicable Method |
| Adjustable according to practical requirement, toluene and isopropyl alcohol can be added to dilute, proper stuffing can be added for sealing materials and heat resistant dope (such as magnesia, quarts powder and isinglass powder) |
| IV Recommended Composition |
FJN-9 Organosilicone Resin（Solid content 50%) |
100 |
#1 Additive |
3~5 |
#4 Accelerant |
0.5~1 |
|
| V Application of Different Assistants |
1.#1 additive can enhance felting and solidifying function of resin
2.#4 accelerant can prevent burning and solidifying function of resin |
| VI Notice |
1. FJN-9 organosilicone resin contains toluene solvent, #1 and #4 assistants contain isopropyl alcohol solvent, these all are dangerous products, fire is forbidden in the process of transportation, storage and application.
2. #1 assistant is alkali products with high corrosion, out of reach of human body, it will deteroprate in the air easily, screw down the cover after application.
3. #4 accelerant is acid chemical with high corrosion, out of reach of human body, screw down the cover after application to prevent metamorphose.
4. Alkalescent #1 addictive can have chemical reaction with acid #4 accelerant easily, then they will lose their former function, therefore add #1 addictive firstly, then add? #4 accelerant after mixing well, it is forbidden to mix the two together directly then add into the resin
5. Pack in 200kg iron barrel or 18kg iron barrel
6. It should be stored in ventilated and dry place in shade to prevent direct sunlight, acid, alkali, fire and heat.
7. Transport conforming to standard of flammable products.
|
|
|
|
|