FJN-9810 High Light Organosilicone Resin |
| I Composition |
| This resin is made of monomer, such as phenyl, methyl chlorosilane and other silicane monomer, made of organic solvent ? |
| II Characteristics and Purpose |
| Compound technique of this resin is advanced with light color, fast dryness, good paint film, high rigidity and heat resistance, fit for making heat resistance high light organic silicon paint. |
| III Main Technical Index |
Item |
Index |
Test Method |
Appearance |
Light yellow transparent liquid, slightly white light is permissible |
GB1721 |
Viscidity(coat-4cups),s 25℃ |
15--30 |
GB1723 |
Solid Content（%） |
50±2 |
GB1724 |
Color FeCo Comparator ≤ |
3 |
GB1722 |
Heat resistance：（500±10℃）4h
FJN-9810:floating type aluminum powder=4:1 |
No crack, no foaming, no shedding |
GB1735 |
Drying Period min |
Surface drying 120 |
GB1728 |
Drying |
180℃ |
60 |
250℃ |
20 |
280℃ |
10 |
|
| IV Instruction |
1. Prevent from acid, alkali, organic salt and amine products or it will be solidified and gelled, performance will be affected.
2. Water, sulfured and other impurity should be contained in thinner of this resin or adhibiting force, dryness and other performance will be affected. |
| V Recommended Compound |
FJN-9810 |
65~75 |
Paint |
8~15 |
Solvent |
8~15 |
Assistants |
1~3 |
|
|
|
|
|