| FJN-9806 Self-dry Environmental Protection Organosilicone Resin |
| I Composition |
| This resin is made of monomer, such as phenyl, methyl chlorosilane and special raw materials, can dissolve to PMA and ethanol, non-toxin and environmental protection resin. |
| II Characteristics and Purpose |
| Compound technique of this resin is advanced, technical index has reached highest standard in China. Dope made of this resin can be dried under normal temperature, especially fit for coating large scale equipment and workpieces that can not be dried to save energy and protect environment. Organic silicon paint made of this resin has excellent paint film, high brightness and high rigidity, especially fit for products that need high environmental protection, such as frying pan, barbecue frame, oven and household apparatus, it can also be made into different heat resistant dope with heat resistant pigment. |
| III Main Technical Index |
Item |
Index |
Test Method |
Appearance |
Light yellow transparent liquid |
GB1721 |
Viscidity(coat-4cups) S |
30-60 |
GB1723 |
Solid Content（%） |
50±2 |
GB1725 |
Drying Period h |
Surface-dry |
2 |
GB1728 |
Completely dry |
24 |
Drying 180℃ |
1 |
Heat Resistance (250±5℃) 500h |
Slightly change the color, no crack, no foaming |
GB1735 |
|
| IV Construction |
1. Prevent from acid, alkali, organic salt and amine products or it will be solidified and gelled, performance will be affected.
2.It is environmental protection type, thinner should adopt PMA, ethanol and ketone products. aromatic hydrocarbon solvent is forbidden, water should not be contained or adhibiting force, dryness and other performance will be affected. |
|
|
|
|