| FJN-9802 High-temperature Organosilicone Resin |
| I Composition |
| Updated product made of phenyl, methyl chlorosilane and special monomer with high-tech |
| II Characteristics and Purpose |
It has excellent performance to high temperature and can be used under 300℃ to 5℃ below zero for long term with high rigidity, fast dryness. It can be combined with organic resin, such as alkyd, crylic acid and epoxy to make different heat resistant dope, as well as H grade insulated paint and different heat resistant release agents
1. FJN-9802 resin can be made into heat resistant dope under 200 to 800℃ with organic resin with high rigidity and fast dryness.
2. FJN-9802R resin can be made into heat resistant dope under 600 to 800℃ with fast dryness, good adhibiting force and excellent flexibility.
3. FJN-9802RS resin can be made into light type heat resistant dope under 400 to 500℃ with high rigidity, good brightnes, excellent adhibiting force and less smoke.
|
| III Main Technical Index |
Item |
Index |
Test Method |
Appearance |
Colorless or Light yellow transparent liquid, no mechanical impurity |
GB1721 |
Viscidity(coat-4cups) S 25℃ |
|
|
FJN-9802 |
15-25 |
GB1725 |
FJN-9802R |
18-35 |
FJN-9802RS |
18-35 |
Solid Content（%） |
50±2 |
GB1723 |
Drying Period h |
Surface Drying |
2 |
GB1728 |
Completely Dry |
24 |
180℃ Drying |
1 |
Heat Resistance（Varnish）
（300℃±5℃）3h |
No color changing, no crack, no foaming, no shedding |
GB1735 |
|
| IV Instruction |
Prevent from acid, alkali, organic salt and amine products, or solidification and gelling will appear, sensitive to alkali products, thus moderate raw materials should be selected for producing the paint.
|
| V Recommended Compound |
9802 |
42~46 |
Organic Resin |
6~10 |
Stuffing |
15~25 |
Paint |
10~20 |
Solvent |
10~20 |
Assistants |
1~3 |
|
|
|
|
|