| FJN-9801 Self-dry Organosilicone Resin |
| I、Composition |
| It is synthesized by phenyl, methyl chlorosilane and special silicane monomer. |
| II、Characteristics and Purpose |
Different heat resistant dopes prepared by this resin can be dried under normal temperature or dried for one hour under 120±5℃, save energy, fit for coating large scale equipment and workpieces which can not be dried with excellent lacquer film, good brightness, high rigidity, high heat resistance, light color and fast dryness which are better for production.
1. FJN-9801A resin can be made into heat resistant dope under temperature from 500 to 600℃
2. FJN-9801B resin can be made into heat resistant dope under 500℃ with good solidifying temperature, fast speed, high rigidity and no viscidity on paint film
3. FJN-9801-400 resin can be made into heat resistant dope under temperature400℃ with good dryness, paint film and brightness.?
4. FJN-9801C resin can be made into heat resistant dope under temperature300℃ with good paint film and brightness.?
5. FJN-9801-1 resin can be made into heat resistant dope which can be dried fast, surface can be dried for about 5minutes, fit for priming paint and surface paint which need fast dryness, and it can be made into fast dry type heat resistant dope.
|
| III、Main Technical Index |
Item |
Index |
Test Method |
Appearance |
Light yellow transparent liquid, light while light is permissible, no mechanical impurity. |
GB1721 |
Color FeCo comparator ≤ |
3 |
GB1722 |
Viscidity(coat-4cups),s |
30-60 |
GB1723 |
Solid Content % ≥ |
50 |
GB1725 |
Heat Resistance: （9801A）
（500±10℃）4h
FJN-9801A:Floating aluminum powder=75:25 |
No foaming, no crack, no shedding, slight color changing |
GB1735 |
Drying Period h |
Surface-dry （Method B） 2 |
GB1728 |
Completely dry （Method A） 24 |
|
| IV、Instruction |
1. It can dissolve into organic solvent, such as toluene, xylene, grease and ketone
2. Prevent from acid, alkali and salt or performance will be affected. |
| V、Recommended Prescription |
FJN-9801A |
52~57 |
Floating Aluminum Plasm |
20~35 |
N-butyl Alcohol |
2~3 |
Oxylene |
Others |
|
|
|
|
|