FJN-1053 Organic Silicone |
| I Composition |
|
This resin is macromolecule polymer after polymerization between hydrolyzation and polymer of methyl chlorosilane and phenyl chlorosilane, as well as polymethyl siloxane type prepolymer.
|
| II Characteristics and Purpose |
| Excellent resistance to high temperature, damp, arc and corona, excellent insulated performance, fit for basic resin of heat resistant dope and special dope, as well as common heat resistant and insulated impregnating varnish, electro-insulating finishing varnish and H grade insulated materials. |
| III Main Technical Index |
Item |
Index |
Appearance |
Light yellow or henna transparent liquid, light while light is permissible, no mechanical impurity. |
Solid Content %： |
50±2 |
Thermal Weight Loss（250℃×3h）%≤ |
5 |
Viscidity（coat-4cups）S 25℃ |
25~60 |
Drying Period（copper patch 200℃）h≤ |
3 |
Heat Resistance （aluminum patch 250℃） 1h≥ |
500 |
|
| IV Instruction |
1. Water, sulfur compound, pyridine and other impurity are forbidden in thinner of silicone or adhibiting force will be affected.
2. There will be a great deal of flammable and explosive products, such as toluene in the production process, enough attention should be paid, operators should be well protected.
3. Acid, alkali, salt and amine compound can speed up solidification of the resin and can affect adhibiting force of the paint film |
| V Storage and Transportation |
1. Pack in galvanized iron barrel, 200kg/barrel
2. Store in ventilated and dry place in shade to prevent from direct sunlight, acid and alkali liquid, fire and heat.
3. Transport as flammable products. |
A |
Resin |
80 |
Aluminum-silver Liquid |
30 |
Xylene |
20 |
N-butyl alcohol |
3 |
|
B |
KH-550 |
60 |
Dehydrated Alcohol |
40 |
|
|
|
|
Proposition |
A：B=100：3 |
|
|